Led using luminescent sapphire as down-converter

ABSTRACT

An LED die includes a luminescent sapphire layer affixed to LED semiconductor layers. The luminescent sapphire absorbs a portion of the primary light and down-converts the primary light to emit secondary light. A phosphor layer may be added. The luminescent sapphire may comprise luminescent sapphire particles in a binder forming a mixture deposited over the LED semiconductor layers. Alternatively, the luminescent sapphire comprises a pre-formed tile that is affixed over the LED semiconductor layers. Alternatively, the luminescent sapphire comprises a luminescent sapphire growth substrate on which is epitaxially grown the LED semiconductor layers. After the LED die is formed, the luminescent characteristics of the sapphire may be adjusted using optical conditioning and/or annealing to tune the die&#39;s overall emission.

CROSS-REFERENCE TO RELATED APPLICATIONS

This application is a division of U.S. application Ser. No. 14/761,115,filed on Jul. 15, 2015, which claims priority from a U.S. ProvisionalApplication Ser. No. 61/753,175, filed on Jan. 16, 2013, by the presentinventor and assigned to the present assignee, incorporated herein byreference.

FIELD OF THE INVENTION

This invention relates to the wavelength conversion of light emittingdiodes (LEDs) and, in particular, to using luminescent sapphire as awavelength conversion material integrated into an LED die.

BACKGROUND

Phosphor-converted LEDs (pcLEDs) are currently employed in a wide rangeof applications, such as for white light LEDs, amber LEDs, etc.Phosphor-converted LEDs comprise an active primary LED light source(typically a III-nitride p-n junction emitting blue light) and a passivesecondary light source (phosphor) that absorbs part of the primary lightand down-converts it to a secondary light of lower energy. Thecombination of the blue light leaking through the phosphor layer and thesecondary light can produce a wide range of colors. Multiple phosphorsmay be used to contribute different wavelengths. The secondary lightsource is not necessarily a phosphor but may be, for example, a quantumdot layer, so we can more generally describe such LEDs as down-convertedLEDs (dcLEDs).

The first white LEDs comprised a blue primary light source (an InGaN/GaNjunction LED die) having a green emitting phosphor coating (Y₃Al₅O₁₂:Ce(YAG)). The Ce activator of the YAG phosphor absorbs a part of the blueprimary light and emits a broad emission centered in the green. Theresulting emission spectrum of the LED is therefore the combination ofblue and green light, appearing white. State of the art LEDs now employa combination of multiple phosphors with a wide range of emissionpossibilities. Typical warm white LEDs contain at least one green andone red emitting phosphor.

The phosphor layer may be formed in a number of ways, such as mixingphosphor powder in a transparent binder (e.g., silicone, glass, epoxy)and depositing the mixture on top of the blue LED die, or attaching apre-formed phosphor tile to the LED die with a transparent adhesive(e.g., silicone), or depositing the phosphor over the LED die usingelectrophoresis. A pre-formed phosphor tile is typically made bysintering phosphor powder under pressure.

It is also known to embed phosphor into a solid transparent matrix(e.g., glass) to create a luminescent substrate, then deposit a seedlayer over the substrate, and then epitaxially grow the LED layers overthe seed layer.

Some drawbacks of the above-mentioned pcLEDs include the following.

The phosphor layer covering the blue LED die induces scattering of theprimary light and thereby reduces the conversion efficiency.

The transparent binders for creating a phosphor mixture, and theadhesives used for attaching a phosphor tile to the LED die, have majordisadvantages, such as having an index of refraction lower than theIII-nitride and the phosphors, which reduces the conversion efficiency,and their thermal conductivity is low, which reduces LED efficacy andreliability.

Substrates infused with phosphor are inadequate substrates for epitaxialgrowth of the III-nitride junction due to lattice mismatches anddifferent coefficients of thermal expansion (CTE). Growing on thesesubstrates requires the deposition of a seed layer, which can reduce thejunction quality and performance, and is expensive. The CTE mismatchesstill remain.

The above-mentioned secondary light sources' intensities and wavelengthscannot be tuned once integrated into the LEDs. This can lead to a largespread in color within the produced LEDs. LEDs not meeting the targetcolor criteria result in a lower production yield and an increase of theoverall LED cost.

SUMMARY

In accordance with the present invention, luminescent sapphire materialis used either as the sole down-converter for the LED primary light oris used in conjunction with other down-conversion materials, such asphosphor or quantum dots. The luminescent sapphire may be in a powderform and deposited over the LED die or may form the growth substrate forthe LED epitaxial layers.

Luminescent sapphire is purely transparent and does not scatter lightpassing through. The substitution, partial or total, of the phosphor bya luminescent sapphire can therefore improve the LED performance.

Sapphire is also a common growth substrate material employed forIII-nitride blue LEDs. A highly efficient p-n junction can therefore begrown using a luminescent sapphire growth substrate without majorchanges in the epitaxial growth process. In one embodiment, because thehigh temperature of epitaxial growth destroys the desired luminescenceproperties of the sapphire, a subsequent annealing step at a lowertemperature is used to reactivate the luminescence centers in thesapphire.

Having the p-n junction directly grown on a luminescent sapphireobviates the need for any binders or adhesives that are conventionallyused to provide a phosphor layer over the top of an LED die. This canlead to a reduced cost, higher conversion efficiency, and higherreliability of the LEDs.

In one embodiment, the LED is a flip chip that generates primary bluelight, and the luminescent sapphire growth substrate generates greensecondary light. The blue light not converted to green light by thesubstrate passes through the transparent substrate.

The overall color of an LED containing luminescent sapphire can be tunedeven after integration of the luminescent sapphire into the LED die.This can be done by modifying the sapphire's optical properties using alaser and/or heat so that the final LED meets the required colorcriteria.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 is a table showing some of the various possible F-centers inluminescent sapphire along with their absorption wavelengths (in nm) andtheir emission wavelengths.

FIG. 2 is a graph showing how the fluorescence of a certain F-center inluminescent sapphire is reduced during annealing over 600° C.

FIG. 3 is a graph showing how the absorption (and creation) of certainF-centers in luminescent sapphire is increased over time duringannealing at 500° C.

FIG. 4 is a graph showing the absorption of various F-centers inluminescent sapphire over a range of wavelengths, with the graphmagnified for wavelengths between 300-700 nm.

FIG. 5 is a flowchart of various steps used to form a dcLED with aluminescent sapphire in accordance with a first embodiment of theinvention.

FIG. 6 is a cross-sectional view of a flip chip LED die with a coatingof a luminescent sapphire mixture over the top of the LED die, inaccordance with the first embodiment of the invention.

FIG. 7 illustrates how the optical properties of the luminescentsapphire in FIG. 6 may be changed after integration with the LED tocolor shift the LED's emission into a target color zone.

FIG. 8 is a cross-sectional view of a flip chip LED die with apre-formed luminescent sapphire tile affixed over the top of the LEDdie, in accordance with a second embodiment of the invention.

FIG. 9 is a flowchart of various steps used to form a dcLED with aluminescent sapphire in accordance with the second embodiment of theinvention.

FIG. 10 is a cross-sectional view of a flip chip LED die with itsepitaxial layers grown over a luminescent sapphire growth substrate, inaccordance with a third embodiment of the invention.

FIG. 11 is a flowchart of various steps used to form a dcLED with aluminescent sapphire in accordance with the third embodiment of theinvention.

Elements that are the same or similar are labeled with the same numeral.

DETAILED DESCRIPTION

Description of Luminescent Sapphire

Sapphire refers herein to the aluminum oxide corundum in the form of asingle crystal. The main chemical composition is Al₂O₃. The sapphire cancontain other elements as dopants and impurities but is still consideredto be sapphire. Single crystals of sapphire are typically grown using avariation of the Czochralski process.

As used herein, the term luminescent sapphire refers to a sapphireexhibiting luminescence corresponding to at least its F₂-like centers,described below.

F-like centers are color centers of the luminescent sapphire. The F-likecenters are defined herein as the different chemical variations of asingle vacancy of oxygen inside the lattice of the sapphire. Such oxygenvacancies are typically created by using a highly reductive atmosphereduring the sapphire crystal growth or the subsequent annealing. Thesapphires containing a high concentration of F-like centers are commonlyreferred as Al₂O₃:C or TCR sapphire (thermochemically reduced).

The most common variations of the F-like centers are the following:

-   -   F center is an oxygen vacancy that trapped two electrons.    -   F⁺ center is an oxygen vacancy that trapped one electron.    -   F(Mg) center is an F center with the presence of one or several        Mg cations surrounding it.    -   F⁺(Mg) center is an r center with the presence of one or several        Mg cations surrounding it.    -   The presence of Mg cations surrounding the F-like centers        results in a shift of the absorption and emission.

The centers identified above are mainly identified by their opticalabsorption and luminescence emission bands as reported in the table ofFIG. 1. FIG. 1 identifies the optical signatures of the known F-like andF₂-like centers in the luminescent sapphire.

We define the F₂-like centers as the different combinations of twoaggregated F-like centers. The well reported variations of F₂-likecenters are the following:

-   -   F₂ center is a cluster of two F centers.    -   F₂ ⁺ center is a cluster of one F⁺ center and one F center.    -   F₂ ⁺(2Mg) center is a cluster of one F₂ ⁺ center with the        presence of two Mg cations surrounding it.    -   F₂ ²⁺ center is a cluster of two F⁺ centers.    -   F₂ ²⁺(2Mg) center is a cluster of one F₂ ⁺ center with the        presence of two Mg cations surrounding it.

Some of the F₂-like centers luminesce (emit) in the visible spectrum(including green) so are the most relevant to the present invention.

The position of the oxygen vacancies respect to each other is identifiedby the anisotropy of the optical absorption bands, shown in FIG. 1. Thepresence of Mg cations surrounding the F₂-like centers results in ashift of the absorption and emission. Furthermore, differentcombinations of the various F₂-like centers may exist in the sapphireand will create slightly different optical features of the sapphire.

Thermal treatment of the sapphire is employed to create the luminescentsapphire. This thermal treatment is referred to as sapphire activation.This treatment creates an aggregation of the F-like centers to form theF₂-like centers to thus create the luminescent sapphire used in thepresent invention.

Optical treatment is employed to tune the emission of the luminescentsapphire. This is referred to as sapphire conditioning. This treatmentmodifies the concentrations of the different F₂-like centers.

Accordingly, the various embodiments of dcLEDs described below usingluminescent sapphire can by tuned to emit a wide variety of colors bysuitable sapphire activation and conditioning.

The creation and destruction of the F₂-like centers in sapphire arethermally activated. FIG. 2 is a graph of the temperature stability of a750 nm emission of luminescent sapphire (secondary light) under 650 nmlaser stimulation (primary light). FIG. 2 shows that the fluorescence(luminescence intensity) of the F₂-like centers that emit at 750 nm (seeFIG. 1 where the F₂ ⁺(2Mg) center has an emission of 750 nm) quicklygoes down after annealing above about 600° C. Although the particularfluorescence wavelength and stimulation wavelength in FIG. 2 aregenerally not used in the LED embodiments, FIG. 2 shows how hightemperatures generally affect the optical properties of the luminescentsapphire.

FIG. 3 is a graph of the absorption coefficient of the 2.87 eV and 4.8eV bands vs. isothermal annealing time at 773K (500° C.). The 2.87 eVand 4.8 eV bands are both shorter wavelengths than typically used inLEDs. FIG. 3 shows the increase of the F₂-like centers' concentrationduring the annealing at 500° C., which correlates to the graphedincrease of the F₂ ²⁺ absorption coefficient. FIG. 3 also shows thesimultaneous decrease of the F⁺ absorption coefficient with anneal time.

As shown by FIGS. 2 and 3, the destruction of the F₂-like centers startsat approximately 600° C. whereas their population can be increased byprolonged annealing of the sapphire at 500° C. During the annealing at500° C., the F⁺ centers aggregate to form F₂ ²⁺ centers. As theannealing time increases, the absorption coefficient of the F₂ ²⁺ centerincreases whereas the absorption coefficient of the F⁺ center decreases.The absorption coefficient correlates to the population of theassociated centers. Such an aggregation step (using heat) is referred toherein as sapphire activation.

FIGS. 2 and 3 were obtained from the papers: Ramirez, R. et al.,Photochromism of vacancy-related defects in thermochemically reducedalpha-Al₂O₃:Mg single crystals, Applied Physics Letters, AIP, 2005, 86,081914; and Ramirez, R. et al., Optical properties of vacancies inthermochemically reduced Mg-doped sapphire single crystals, Journal ofApplied Physics, AIP, 2007, 101, 123520, both incorporated herein byreference.

The role of the Mg is reported to help aggregation of the F₂-likecenters. Such sapphire is also referred to Al₂O₃:C,Mg. Sapphire may begrown, using known methods, to have the Al₂O₃:C,Mg composition.

One of the reported properties of the F₂-like centers in sapphire isphotochromic conversion under sufficient photon irradiance fluxes. It isreported that the excitation of the luminescent sapphire by a high peakpower laser at a wavelength of 440 nm can decrease the concentration ofthe blue-absorbing/green-emitting F₂ ²⁺(2Mg) centers and increase the F₂⁺(2Mg) center (equation 1 below). This is an optical treatment of thesapphire that further tunes its fluorescent properties. Theconcentrations of other centers simultaneously change such that thecharge balance remains respected. It is also reported that theconcentration of the F₂ ²⁺(2Mg) centers can be increased by exciting theluminescent sapphire with a high peak power laser at a wavelength of 330nm (equation 2).

Such tuning of the F₂-like centers concentrations by optical treatmentis herein defined as sapphire conditioning.

F₂ ²⁺(2Mg)+hυ₄₄₀→F₂ ⁺(2Mg)+other centers   (eq. 1)

F₂ ⁺(2Mg)+hυ₃₃₀→F₂ ²⁺(2Mg)+other centers   (eq. 2)

The sapphire's photochromism properties are not restricted to 440 nm and330 nm excitation. Other wavelengths, preferentially at the absorptionbands of the F₂-like centers, can be employed. The underlying “2-photonabsorption process” controlling the photochromism properties is welldescribed in literature and need not be described herein.

In one embodiment, the sapphire is subject to activation (thermal) andconditioning (optical) to absorb some of the blue primary lightgenerated by the LED's pn junction and emit green secondary light. Theprecise activation and conditioning depends on the peak wavelength ofthe primary light, the thickness/density of the sapphire, the targetcolor point, and other factors. The required activation and conditioningto achieve the target color may be determined empirically for aparticular application. A red phosphor may then be added on top of theLED to create white light.

FIG. 4 is a graph of absorption vs. wavelength for F, F⁺, and F₂ ⁺(2Mg)centers for Al₂O₃:C,Mg and Al₂O₃:C. The inset is a magnified view forwavelengths 300-700 nm. Curve 20 is for sapphire “bleached” with 435 nmlaser light (sapphire conditioning), and curve 22 is for sapphire “asgrown” or annealed. FIG. 4 was taken from the following papers:Akselrod, M. S. et al., New aluminum oxide single crystals forvolumetric optical data storage, Optical Data Storage 2003, Optical datastorage, SPIE, 2003, 5069, 244-251; and Akselrod, M. S. et al.,Fluorescent aluminum oxide crystals for volumetric optical data storageand imaging applications, J. Fluoresc., 2003, 13, 503-511, bothincorporated herein by reference.

Of particular interest is the wavelength range of about 450-650 nm,which generally includes the blue to red range.

Although the properties, creation, and adjustment of luminescentsapphire are well known, the inventor is unaware of any integration ofluminescent sapphire in an LED die for down-conversion.

Conversion efficiency (CE) is the luminous flux (lm) emitted by the LED(including the down-converted light) per amount of primary source light.The CE is a good ruler of the efficiency of the secondary source (theluminescent material) and its integration in the LEDs. In the followingembodiments, using the luminescent sapphire as a down-converter, the CEof the resulting LED is improved vs. the CE of a pcLED.

Embodiment 1

In a first embodiment, the luminescent sapphire is used in powder forminstead of, or in addition to, using a phosphor powder. An example ofthis first embodiment is represented by FIGS. 5 and 6.

As a preliminary matter, bulk luminescent sapphire (Al₂O₃:C,Mg orAl₂O₃:C, depending on the wavelengths of interest) is grown usingconventional techniques, and the sapphire is activated and conditioned,as described above and in accordance with known techniques, to have thedesired light absorption and emission properties for the particularapplication (e.g., LED die and target color). Empirical testing may beperformed to achieve the target absorption and emission properties. Thetarget absorption wavelength will be the peak wavelength emission of theactual LED pn junction (the active layer) used and will typically be inthe visible blue range of wavelengths. In one embodiment, the emissionof the luminescent sapphire is green when energized with the blue LEDlight. Accordingly, adding a red phosphor layer will create warm whitelight.

In step 24 of FIG. 5, the luminescent sapphire crystal is subject to agrinding process and sieved to the desired range of particle size. Anacceptable range of particle size distribution D50 is 10 to 50 μm.Particle size distribution D50 is also known as the median diameter ofthe particle size distribution and is the value of the particle diameterat 50% in the cumulative distribution.

In step 26, the luminescent sapphire powder is infused into atransparent matrix (such as silicone), with appropriate and conventionaladditives, and homogeneously mixed. The chosen additives depend on theapplication and may include phosphor powders, dispersants, etc.

In step 28, the mixture is integrated into the LED so as it can absorbthe primary light and down-convert it to the desired secondary light.For example, the mixture can be integrated by lamination (e.g., forminga pre-formed sheet or tile and affixing it over the LED wafer or die),overmolding (e.g., placing LED dies mounted on a wafer in individualmold indentions filled with the mixture and then curing the mixture), orspray-coating the mixture over at least the top surface of the LED die.The result is a dcLED characterized by a certain color point. The dcLEDmay or may not include phosphor in the mixture or as a separate layer.

FIG. 6 is a cross-sectional view of one type of LED (a flip chip) withthe luminescent sapphire mixture deposited over the LED's semiconductorsurface as a luminescent sapphire layer 30 and cured. Other type of LEDsmay be used, such as vertical LEDs, lateral LEDs, etc. In the example,an N-type layer 32 is epitaxially grown over a sapphire growth substrate(which has been removed by laser lift-off), an active layer 34 isepitaxially grown over the N-type layer 32, and a P-type layer 36 isepitaxially grown over the active layer 34. The layers 34 and 36 areetched to expose the N-type layer 32, and metal contacts 38 and 40 aredeposited to electrically contact the P-type layer 36 and N-type layer32, respectively. The LED die is then mounted on a submount 42 or othersubstrate. The submount 42 has metal pads that are directly bonded tothe metal contacts 38 and 40, and the pads are ultimately electricallyconnected to a power source.

The exposed surface of the N-type layer 32 may be roughened to improvelight extraction prior to the luminescent sapphire layer 30 beingdeposited.

In prior art LEDs using only a phosphor for down-conversion, if thetarget color point is not achieved, the LED is either rejected ordowngraded to a lower quality LED. This increases the overall cost ofLED production.

However, by using a luminescent sapphire layer 30 overlying the N-typelayer 32, the color point of the dcLED may be adjusted after the dcLEDis energized and tested while bonded to the submount 42 or while inwafer form and probed. The testing may also be performed using anexternal energizing light source. The color point adjustment may be bysapphire conditioning (step 46), where the photochromic properties ofthe luminescent sapphire layer 30 are adjusted using a high peak powerlaser to create a color shift. Additional detail is provided below. Thispost-integration adjustment increases the production yield of dcLEDs(and therefore decreases the cost of production) and improves the colorpoint control.

Finally, other additional optics, such as a transparent dome lens (notshown), can be placed or molded over the dcLED in order to improve thelight extraction of the dcLED.

If the above process has been performed on a wafer scale, the LEDdies/submounts are then singulated.

There may be one or more other layers between the LED semiconductorlayers and the luminescent sapphire layer 30.

Practical Example of Embodiment 1

A luminescent sapphire rich in blue-absorbing/green-emitting F₂ ²⁺(2Mg)centers is ground and sieved to a particle size in the range 20 to 40μm. The powder is mixed with silicone and a red phosphor in suchproportion to cause the resulting dcLED color point to be a warm white3000K color temperature. The silicone employed is transparent andpreferentially has an index of refraction greater than 1.50. The redphosphor used is, for example, a member of the phosphor family(Ca,Sr)AlSiN₃:Eu or the phosphor family (Ba,Sr)Si₅N₈:Eu. The slurrysilicone+luminescent sapphire powder+red phosphor is homogeneously mixedto form the down-converter mixture (layer 30 in FIG. 6). In order tocreate the desired warm white pcLED, the mixture is integrated with aprimary blue source: for example, blue-emitting GaN-based LED diesemitting a peak wavelength between 440 to 460 nm. These dies may bebased on thin-film flip chip technology and have an InGaN/GaN p-njunction. Other types of LEDs may be used.

A well-controlled volume of the mixture is dispensed above the die usingany conventional deposition process, normally used for dispensing aphosphor mixture. The mixture is then cured by heat or UV. At thisstage, the color point of some LEDs can be outside of the targeted zonefor a 3000K LED.

In the example, of FIG. 7, the circle 50 represents an acceptable rangeof color points (the target zone) that the final dcLED should exhibit.The u′ and v′ axes represent the coordinates in the CIE 1976 colorsystem. Point 52 represents the color point of the LED(s) measured aftertesting after step 28 in FIG. 5. A high power pulsed laser is then usedto shift the color point to the point 54 within the circle 50 during theconditioning step 46 in FIG. 5. The proper conditioning may bedetermined empirically. The testing and conditioning may be performedautomatically using a look-up table cross-referencing the measured colorpoint to the required conditioning for shifting the color emission towithin the target zone circle 50. The required laser power and/orduration are then determined (also by the look-up table), and theconditioning is performed. The conditioning may be performedincrementally, with testing after each incremental step to ensure thereis no over-compensation.

If there is too much secondary light generated by the luminescentsapphire, the required adjustment could be obtained by decreasing thedown-conversion power of the luminescent sapphire. This can be performedby reducing the concentration of F₂ ²⁺(2Mg) centers in the luminescentsapphire during a conditioning step. For this, the luminescent sapphirecan be exposed to a high peak power laser at a wavelength of 440 nm fora period of time, determined empirically. See equations 1 and 2 above.

Other adjustments can be used to create a precise color emission suchthat the LEDS need not be “binned.”

Embodiment 2

In a second embodiment, shown in FIGS. 8 and 9, the luminescent sapphireis integrated as a pre-formed single crystal tile that is attached tothe top surface of the primary light source.

In FIG. 8, the primary light source LED is similar to that of FIG. 6where an N-type layer 32 is epitaxially grown over a sapphire growthsubstrate, an active layer 34 is epitaxially grown over the N-type layer32, and a P-type layer 36 is epitaxially grown over the active layer 34.The layers 34 and 36 are etched to expose the N-type layer 32, and metalcontacts 38 and 40 are deposited to electrically contact the P-typelayer 36 and N-type layer 32, respectively. The sapphire grows substrateis removed by laser lift-off and the exposed surface of the N-type layer32 may then be roughened. The LED die is then mounted on a submount 42or other substrate. The submount 42 has metal pads that are directlybonded to the metal contacts 38 and 40, and the pads are ultimatelyelectrically connected to a power source.

An adhesive layer 58, such as silicone, is deposited over exposed N-typelayer 32. A luminescent sapphire tile 60 is then positioned and pressedon the adhesive layer 58. An optional optical features layer 62 may thenbe positioned or molded over the tile 60, such as a filter layer or atextured layer for improving light extraction. An optional phosphorlayer 64 (e.g., red phosphor in a silicone binder) may then be depositedfor further color point adjustment. The laser exposure step forconditioning the tile 60 may be performed prior to the layers 62 and 64being deposited. The laser exposure step may be performed on the tile 60before or after the tile 60 is affixed to the LED. All steps may beperformed on a wafer scale on a submount wafer populated with an arrayof LED dies.

In another embodiment, the luminescent sapphire tile 60 comprisesluminescent sapphire particles in a cured binder.

FIG. 9 identifies various steps for fabricating the device of FIG. 8.

A flat luminescent sapphire crystal wafer is first formed (step 68) andthen cut into tiles (step 70) with a size generally corresponding to theprimary source LED (e.g., 1 mm²). The tile 60 (typically beforesingulation) is then conditioned (step 72) using a laser such that itpresents the targeted concentration of the desired F₂-like color centers(see equations 1 and 2 above).

The tile 60 is then attached to the LED die using an adhesive layer(step 74).

At this stage, different options can be executed:

-   -   a. No other phosphors are added to the device, whereby all the        down-converted emission is performed by the luminescent sapphire        tile 60. A conditioning step can be further employed to correct        the color point if necessary. In one example, the green emission        is increased by increasing the population of F₂ ²⁺(2Mg))        centers.    -   b. An optical features layer 62, such as a dichroic filter, may        be deposited (step 76) over the tile 60 in order to control the        emission (angular and spectral).    -   c. One or more phosphors may be dispensed over the tile 60 (step        78) to form the phosphor layer 64 in FIG. 8. The optical        features layer 62, such as a dichroic filter can be optionally        deposited in between the phosphor layer 64 and the tile 60. The        conditioning step 80 can optionally be used to correct the LED        color point while taking the phosphor contribution into account.        For example, a warm white LED with a color temperature of 3000K        could be fabricated by integrating a red-emitting phosphor layer        64 over the tile 60.    -   d. Same as version c but with the integration of the phosphor        layer over the LED die first and then adhesion of the        luminescent sapphire tile 60 over the phosphor layer. The        optical features layer and/or the conditioning step can further        be applied before encapsulation of the device.

Embodiment 3

In a third embodiment, the luminescent sapphire is used as a growthsubstrate on which the LED semiconductor layers are epitaxially grown asillustrated in FIGS. 10 and 11.

First, as shown in FIG. 11, a sapphire single crystal is chosen suchthat it contains the desired F-like centers (step 84). The sapphiresingle crystal is prepared as a growth substrate 86 (FIG. 10) by beingcut and polished to allow epitaxial growth on it.

In step 88, the III-nitride p-n junction (layers 32, 34, 36) is grown onone side of the sapphire substrate 86. During this step, the temperatureinside the growth reactor is maintained between 700 and 1100° C. forseveral hours under a reducing atmosphere. At such temperature and time,the luminescent F₂-like centers of the sapphire are destroyed (see FIG.2). Therefore, it is pointless to use a luminescent sapphire as a growthsubstrate unless the centers can be reactivated.

After the epitaxial growth, the wafers are removed from the reactors. Anannealing for several minutes in the range 500 to 600° C. is thenperformed in order to activate the P-dopants in the P-type layer 36 ofthe III-nitride junction (step 90). This annealing is performed in anoxygen-containing atmosphere.

Further at this stage of the process, the sapphire substrate 86containing F-like centers is activated (step 92) to create a luminescentsapphire. Physically, the sapphire activation creates an aggregation ofF-like centers to form F₂-like centers. The sapphire substrate 86 can beactivated by an annealing or several annealings at a temperature withinthe range 300-700° C. (below the epitaxial growth temperature). Forexample, the sapphire substrate 86 can be activated by annealing thewafer at a temperature of 500° C. for several hours as published in theliterature. The concentration of F₂-like centers can be controlled byadjusting the annealing time and temperature. Furthermore, the sapphiresubstrate 86 activation leads to the creation of many types of F₂-likecenters. If only one particular species of F₂-like center is of interestfor down-conversion, then the desired F₂-like center concentration canbe obtained by applying a conditioning (laser) step 94 to the sapphiresubstrate 86. For example, the concentration of theblue-absorbing/green-emitting F₂ ²⁺(2Mg) centers can be increased byexciting the sapphire substrate 86 with a high peak power laser at awavelength of 330 nm. The quality of such conditioning can be controlledby, for example, measuring the fluorescence intensity generated by theF₂ ²⁺(2Mg) centers of the luminescent sapphire under excitation at 450nm (e.g., by an external source or by energizing the LED).

Once the targeted concentration of desired F₂-like centers is obtained,the wafer can return to the normal fabrication process for the LEDs,progressing from conventional wafer fab steps (grouped into step 96) todie fab steps (grouped into step 98) to phosphor integration (step 100).During these subsequent steps, the temperature is held below 600° C. andthe activation of the sapphire substrate 86 is therefore preserved.

Optionally, more conditioning steps 102 and 104 can be added during theprocess in order to take advantage of photochromic properties of theluminescent sapphire. A conditioning step 102 could be performed afterthe singulated die is attached to a submount wafer in order to adjustthe concentration of desired F₂-like centers for the actual primarylight source efficiency and wavelength and reduce the v′ dispersion ofthe produced LED population. Another conditioning step 104 could beundertaken after the phosphor integration step 100 in order to tune thecolor point as described in Embodiment 1.

Optical features (step 106) may also be added to the LED die.

FIG. 10 shows an optical features layer 108 and a phosphor layer 110,such as a dichroic filter layer and a red phosphor layer for creatingwhite light. The filter layer may reflect the red light from thephosphor layer 110 but allow the shorter wavelength light to pass toavoid absorption of the red light by the LED.

In addition to the various benefits described above, by performing alldown-conversion by the luminescent sapphire and not using phosphor, theLED may be used in harsh environments for many years such as inautomobile headlamps. Phosphor is very sensitive to moisture and mayultimately degrade in a headlamp environment.

The following references identify the state of the art in luminescentsapphire and exemplify what one skilled in the art is aware of Suchreferences illustrate that one skilled in the art, after reading thepresent disclosure, is able to manufacture the luminescent sapphire andperform the required activation and conditioning to achieve the targetcolor point of a dcLED. Such references are incorporated herein byreference.

-   -   1. Akselrod, M. S. et al., New aluminum oxide single crystals        for volumetric optical data storage, Optical Data Storage 2003,        Optical data storage, SPIE, 2003, 5069, 244-251    -   2. Akselrod, M. S. et al., Fluorescent aluminum oxide crystals        for volumetric optical data storage and imaging applications, J.        Fluoresc., 2003, 13, 503-511    -   3. Akselrod, M. S. & Akselrod, A. E, New Al₂O₃:C,Mg crystals for        radiophotoluminescent dosimetry and optical imaging, Radiat.        Prot. Dosimetry, 2006, 119, 218-221    -   4. Ramirez, R. et al., Electroluminescence in magnesium-doped        Al₂O₃ crystals, Radiation Effects and Defects in Solids, 2001,        154, 295-299    -   5. Ramirez, R. et al., Photochromism of vacancy-related defects        in thermochemically reduced alpha-Al₂O₃:Mg single crystals,        Applied Physics Letters, AIP, 2005, 86, 081914    -   6. Ramirez, R. et al., Optical properties of vacancies in        thermochemically reduced Mg-doped sapphire single crystals,        Journal of Applied Physics, AIP, 2007, 101, 123520    -   7. Sykora, G. et al., Novel Al₂O₃:C,Mg fluorescent nuclear track        detectors for passive neutron dosimetry, Radiation Protection        Dosimetry, 2007, 126, 1-4    -   8. Sykora, G. et al., Spectroscopic properties of novel        fluorescent nuclear track detectors for high and low LET charged        particles, Radiation Measurements, 2008, 43, 422-426    -   9. Sykora, G. et al., Properties of novel fluorescent nuclear        track detectors for use in passive neutron dosimetry, Radiation        Measurements, 2008, 43, 1017-1023    -   10. Sykora, G. J. & Akselrod, M. S., Photoluminescence study of        photochromically and radiochromically transformed Al₂O₃:C,Mg        crystals used for fluorescent nuclear track detectors, Radiation        Measurements, 2010, 45, 631-634    -   11. Tardio, M. et al, High temperature semiconducting        characteristics of magnesium-doped alpha-Al₂O₃ single crystals,        Applied Physics Letters, AIP, 2001, 79, 206-208    -   12. Tardio, M. et al, Electrical conductivity in magnesium-doped        Al2O3 crystals at moderate temperatures, Radiation Effects and        Defects in Solids, 2001, 155, 409-413    -   13. Tardio, M. et al, Photochromic effect in magnesium-doped        alpha-Al₂O₃ single crystals, Applied Physics Letters, AIP, 2003,        83, 881-883    -   14. Tardio, M. et al, Enhancement of electrical conductivity in        alpha-Al[sub 2]O[sub 3] crystals doped with magnesium, Journal        of Applied Physics, AIP, 2001, 90, 3942-3951    -   15. Tardio, M. et al, Electrical conductivity in undoped        alpha-Al2O3 crystals implanted with Mg ions, Nuclear Instruments        and Methods in Physics Research Section B: Beam Interactions        with Materials and Atoms, 2008, 266, 2932-2935

While particular embodiments of the present invention have been shownand described, it will be obvious to those skilled in the art thatchanges and modifications may be made without departing from thisinvention in its broader aspects and, therefore, the appended claims areto encompass within their scope all such changes and modifications asfall within the true spirit and scope of this invention.

What is claimed is:
 1. A light emitting device comprising: lightemitting diode (LED) semiconductor layers comprising an N-type layer, anactive layer emitting primary light, and a P-type layer; and luminescentsapphire, which is not a growth substrate for the semiconductor layers,affixed over a light emitting surface of the LED semiconductor layers,the LED semiconductor layers and the luminescent sapphire forming partof an LED die, the luminescent sapphire containing oxygen vacanciesresulting in F-like centers having defined optical absorption andluminescence emission bands, wherein the luminescent sapphire absorbs aportion of the primary light and down-converts the primary light to emitsecondary light, via the F-like centers, such that an emission from theLED die includes at least a combination of the primary light and thesecondary light.
 2. The device of claim 1 wherein the luminescentsapphire comprises luminescent sapphire particles combined with a binderto form a mixture, wherein the mixture is located overlying the lightemitting surface of the LED semiconductor layers.
 3. The device of claim2 wherein the mixture is laminated over the semiconductor layers.
 4. Thedevice of claim 2 wherein the mixture is molded over the semiconductorlayers.
 5. The device of claim 2 wherein the mixture is located directlyon one of the LED semiconductor layers.
 6. The device of claim 1 whereinthe luminescent sapphire comprises a pre-formed tile that is affixedover the light emitting surface of the LED semiconductor layers.
 7. Thedevice of claim 6 wherein the tile comprises a single crystal of theluminescent sapphire.
 8. The device of claim 6 wherein the tilecomprises luminescent sapphire particles in a binder.
 9. The device ofclaim 6 wherein the tile is directly affixed to one of the LEDsemiconductor layers with an adhesive layer.
 10. The device of claim 1wherein the N-type layer, the active layer, and the P-type layer areepitaxially grown over a sapphire growth substrate, which is not theluminescent sapphire.
 11. The device of claim 1 further comprising aphosphor layer overlying the LED semiconductor layers as part of the LEDdie, such that a light emission of the LED die comprises the primarylight, the secondary light from the luminescent sapphire, and light fromthe phosphor layer.
 12. The device of claim 11 wherein the luminescentsapphire comprises luminescent sapphire particles combined with a binderto form a mixture, wherein the mixture is located overlying the lightemitting surface of the LED semiconductor layers, and wherein thephosphor is part of the mixture.
 13. The device of claim 12 wherein theprimary light is blue light, and the secondary light and light from thephosphor include green and red light.
 14. The device of claim 1 whereinthe primary light, the secondary light from the luminescent sapphire,and the light from the phosphor layer create white light.
 15. A methodcomprising: providing a light emitting diode (LED) die comprising LEDsemiconductor layers generating primary light; affixing a luminescentsapphire layer over a light emitting surface of the LED semiconductorlayers, wherein the luminescent sapphire layer is not a growth substratefor the semiconductor layers, the luminescent sapphire down-convertingsome of the primary light to secondary light, such that light emitted bythe LED die comprises at least a combination of the primary light andthe secondary light, the luminescent sapphire comprising oxygenvacancies resulting in F-like centers having defined optical absorptionand luminescence emission bands; and conditioning the luminescentsapphire layer in the LED die using a laser to adjust a characteristicof the secondary light.
 16. The method of claim 15 further comprisingactivating the luminescent sapphire in the LED die by annealing theluminescent sapphire to increase its luminescent properties after theLED die is formed.
 17. The method of claim 15 wherein the luminescentsapphire comprises luminescent sapphire particles in a binder forming amixture, wherein the mixture is located overlying the light emittingsurface of the LED semiconductor layers.
 18. The method of claim 17wherein phosphor particles are also included in the mixture.
 19. Themethod of claim 15 wherein the luminescent sapphire comprises apre-formed tile that is affixed over the light emitting surface of theLED semiconductor layers.
 20. The method of claim 15 further comprisingdepositing a phosphor layer over the LED semiconductor layers, whereinthe primary light, the secondary light from the luminescent sapphire,and the light from the phosphor layer create white light.